- Plastic Flooring[10]
- Other Interior Accessories[4]
- Plastic Sheets[10]
- Decorative Films[6]
- Plastic Film[1]
- Table Cloth[7]
- Home Appliance Plastic[2]
- 100% Polyester Fabric[1]
- Rubber Flooring[2]
- Other Flooring[1]
- Anti-Static Flooring[3]
- Blanket[9]
- Carpet[4]
- Food Additives[8]
- Monosodium Glutamate[1]
- Flavour & Fragrance[4]
- Organic Intermediate[1]
- Starch[10]
- Chlorate[10]
- Chemical Auxiliary Agent[1]
- Sunflower Kernels[4]
- Fresh Ginger[1]
- Fresh Garlic[2]
- Peanuts[2]
- Vegetable Seeds[1]
- Loaders[3]
- Cast & Forged[9]
- Other Machinery[1]
- Casting Services[1]
- Other Shooting Products[5]
- Other Toys & Hobbies[1]
- Mats & Pads[1]
- Other Metals & Metal Products[1]
- Contact Person : Ms. Zhang Eva
- Company Name : Zhengzhou United Asia Trading Co., Ltd.
- Tel : 86-371-65675292
- Fax : 86-371-65801210
- Address : Henan,Zhengzhou,No 299, Jinshui Rd, Zhengzhou City, China
- Country/Region : China
- Zip : 450008
Agent for steel, spheroidizing agent
Related Product Searches:Agent for steel, spheroidizing agent,High Quality,Ferro silicon powder,Silicon metal
Appearance: silver gray section, block, not powder
Melting pint: 980-1180°C
Specific gravity: 4.0-4.1
Granularity: 5-30mm, smaller than 5mm and larger than 30mm of it does not surpass 5% of the total weight
Advantage: strong nodularization, stable composition, smooth reaction, no recession worries. the slag content produced during the nodulizing period is small, which is only 1/8 of slag content produced ; the nodulizing cost is lower than common nodulizer.
Application:
1. We produce all kinds of ductile cast iron for the various plate of RE-Si-MG alloy nodularizer, After added to the molten iron, it can play the role of nodularization, desulphurization, degas, etc.
2. It can increase the purity of the cast water, and wit arsenic, zinc, it can generates compounds, which are insoluble in iron and low melting point. Remove these impurities can prevent the interference of nodularization damage.
| Plate | Chemical compositions (%) | ||||||
| Re | Mg | Ca | Si | Mn | Ti | Fe | |
| ≤ | |||||||
| FeSiMg6RE1 | 0.5-2.0 | 5.0-7.0 | 1.5-3.0 | 44.0 | 1.0 | 1.0 | The rest |
| FeSiMg7RE1 | 0.5-2.0 | 6.0-8.0 | ≤1.5 | 44.0 | 1.0 | 1.0 | The rest |
| FeSiMg7RE3 | 2.0-4.0 | 6.0-8.0 | 2.0-3.5 | 44.0 | 1.0 | 1.0 | The rest |
| FeSiMg8RE3-A | 2.0-4.0 | 7.0-9.0 | ≤2.0 | 44.0 | 1.0 | 1.0 | The rest |
| FeSiMg8RE3-B | 2.0-4.0 | 7.0-9.0 | 2.0-3.5 | 44.0 | 1.0 | 1.0 | The rest |
| FeSiMg8RE5 | 4.0-6.0 | 7.0-9.0 | ≤3.0 | 44.0 | 2.0 | 1.0 | The rest |
| FeSiMg8RE7 | 6.0-8.0 | 7.0-9.0 | ≤3.0 | 44.0 | 2.0 | 1.0 | The rest |
| FeSiMg10RE7 | 6.0-8.0 | 9.0-11.0 | ≤3.0 | 44.0 | 2.0 | 1.0 | The rest |
| FeSiMg9RE9 | 8.0-10.0 | 8.0-10.0 | ≤3.0 | 44.0 | 2.0 | 1.0 | The rest |
| FeSiMg8RE18 | 17-20.0 | 7.0-10.0 | ≤3.0 | 42.0 | 4.0 | 2.0 | The rest |
Agent for steel, spheroidizing agent